PVC Foam Sheet
PVC FOAM board is becoming the substitution of wood in many fields such as AD and Decoration and Furniture. It made through foaming and pressing into shape with additives. The main material is PVC. So it covers not only features of wood plats, but also very light and can be printed, engraved easily.
Specific Properties
- Low thermal conductivity, good insulation
- Resistant to chemicals and corrosion
- Absorbs vibration and oscillation
- Weather resistant
- Low absorption of water
- Low flammability
- Highly suitable for printing and foiling
Processing Performance
- It can be processed by drilling, sawing, nailing, planning and bonding
- It can be in Hot-Forming, Hot-Bending and Hot-Folding
- The surface is very smooth and suitable for printing
- It can be welded and bonded with other PVC materials
Standard or Fire-Proof Panels?
The default panels we use for the manufacturing of our systems, are the “Regular Panels”. If your project requires “Fire-Proof Panels”, then please make sure you request that at the beginning of your order procedure.
| PROPERTY | TEST METHOD | UNITS | REGULAR PANELS | FIRE-PROOF PANELS |
|---|---|---|---|---|
| Density | DIN 53479 | g/cmᶟ | 0.55 | 0.55 |
| Hardness | DIN 53505 | Shore ‘D’ | ≥ 42 | ≥ 42 |
| Water Absorption | DIN 53495 | % | ≤ 1.0 | ≤ 1.0 |
| Tensile strength* | DIN 53455 | MPa | ≥ 15 | ≥ 15 |
| Elongation at break** | DIN 53455 | % | ≥ 15 | ≥ 15 |
| Modulus of elasticity | DIN 53457 | MPa | 900 – 1500 | 900 – 1500 |
| Impact strength Izod | ASTM D 256 | KJ/m² | ≥ 9.0 | ≥ 9.0 |
| Impact strength Charpy | DIN 53253 | KJ/m² | ≥ 15 | ≥ 15 |
| Flexural strength | DIN 53452 | MPa | > 32 | > 32 |
| Compressive Strength at 10% Deformation | DIN 53421 | MPa | > 6.5 | > 6.5 |
| Surface resistivity | ASTM D 257 | Ω | > 1 x 1014 | > 1 x 1014 |
| Volume resistivity | ASTM D 257 | Ω-cm | > 1 x 1015 | > 1 x 1015 |
| Dielectric Constant at 1 MHZ | ASTM D 150 | F/m | 1.56 | 1.56 |
| Dielectric strength | DIN 53481 | KV/cm | ≥ 90 | ≥ 90 |
| Vicat softening temperature | DIN 53460 | °C | ≥ 73 | ≥ 73 |
| Heat Deflection temperature @ 1.8 MPa | DIN 53461 | °C | 58 | 58 |
| Coefficient of Linear Expansion | DIN 53752 | mm/m °C | 0.08 | 0.08 |
| Thermal conductivity | DIN 52616 | W/m K | 0.05 | 0.05 |
| Smoke Production | EN 13501-1 | FIGRA 0,2 (W/s) FIGRA 0,4 (W/s) | Class B | Class B |
| EN 13501-1 | SMOGRA (m²/s) | CLASS s2 | CLASS s1 | |
| Flaming Droplets | EN 13823 | pc | CLASS d0 | CLASS d0 |